Optical and electrical properties of ITO film on flexible fluorphlogopite substrate

Indium Tin Oxide (ITO) films were prepared, at room temperature, on a fluorphlogopite substrate using magnetron sputtering technology. At various temperatures of 500 °C, 600 °C, 700 °C, 800 °C, and 900 °C, the samples were (had) annealed for 2 h (a 2-h duration). The results showed improvement in the crystalline performance of ITO film at selected annealing temperatures, with a significant reduction in resistivity at 800 °C. The lowest resistivity is 4.08 × 10^?4 Ω-cm, which is nearly an order of magnitude lower than the unannealed sample. All samples have an average light transmittance above 85% in the visible light range (400–800 nm), and with increasing annealing temperature, the average light transmittance tends to decrease. Besides, at the sensitive wavelength of 550 nm, the light transmittance is as high as 93.74%. The sheet resistance testing of the sample was through the number of bending times, which revealed that with the increase of the number of bending, the sheet resistance increases. However, after 1200 bending times, the change rate of the sheet resistance remains below 5%. Thus, the ITO film prepared on the flexible fluorphlogopite substrate revealed excellent optical and electrical properties, good flexibility, and improved stability after high-temperature annealing, which guarantees successful application in flexible electronic devices.     

Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

Characteristics of reaction and product microstructure during light calcination of magnesite in transport bed

A gas-heating laboratory transport bed was adopted to simulate the industrial transportbed reactor for flash calcination of magnesite, and a method based on TG analysis of a reacted sample was further developed to calculate the decomposition rate or conversion of its containing MgCO₃. The study investigated how the conversion and product reactivity as well as microstructure vary with reaction conditions including temperature, particle size and times of re-calcination for powder magnesite. Magnesite powder (<150 μm) calcination is a quick reaction that reaches 98% decomposition of its containing MgCO₃ in 1—2 s,corroborating the feasibility of magnesite flash-calcination in transport bed reactors. The coloration time given by the citric acid chromogenic method was 17—55 s and 294 s for the obtained products from transport and fixed beds, respectively. This proves the obviously higher activity and thus improved microstructure of the product from transport bed. During the calcination process, the MgO grain size of the product gradually increases, and the surface structure changes from loose and porous to dense and smooth. This structural change can be completed within a few seconds.     

煤基高能量密度燃料的合成及表征

高能量密度燃料是为新型高性能飞行器提供动力保障的关键,其合成及应用研究具有重要的前瞻性和重大战略意义。煤炭是我国的主体能源和重要原料,通过煤直接转化获取的煤基油,充分保留了煤中特有的环状分子化学结构,具有良好的热安定性和较高的能量密度,被认为是高超音速飞行器的优选燃料。以煤直接液化工艺生产的煤液化石脑油馏分为起始原料,通过富集轻质芳烃、化学合成、催化加氢稳定和产物分离提纯等方法制备煤基高能量密度燃料,并对其产物进行分子结构表征和性能评价。结果表明,煤直接液化生产的石脑油馏分是一种优异的催化重整原料,经催化重整富集轻质芳烃后,其轻质芳烃质量分数高达71.05%。Diels-Alder化学合成主产物是由多个封闭环平面组成且具有空间立体构型的二环或三环烃类物质,质量分数为46.18%,因分子内存在较大的张力能,结构紧凑,其拥有更大的密度和体积热值。煤基高能量密度燃料的密度和体积热值分别为0.8990 g/cm3与38.06 MJ/L,均大大超过现行的国内石油基喷气燃料(RP-3和RP-6)、煤基大比重喷气燃料、美国和俄罗斯军用标准。与单一纯物质合成高能量密度燃料(JP-10和T-10)比较,其密度与体积热值偏小。究其原因主要是轻质芳烃的富集度仅为71.05%,需进一步提高其轻质芳烃质量分数。另外,制备的煤基高能量密度燃料种类复杂,其主产物质量分数仅46.18%,下一步可重点调控合成产物的分子构型和纯化分离。     

Increasing the photocatalytic and fungicide activities of Ag3PO4 microcrystals under visible-light irradiation

The present study reports for the first time the performance of silver phosphate (Ag₃PO₄) microcrystals as photocatalyst (degradation of Rodamine B-RhB) and antifungal agent (against Candida albicans–C. albicans) under visible-light irradiation (455 nm). Ag₃PO₄ microcrystals were synthesized by a simple co-precipitation (CP) method at room temperature. The structural and electronic properties of the as-synthetized Ag₃PO₄ have been investigated before and after 4 cycles of RhB degradation under visible light using X-ray diffraction (XRD), micro-Raman spectroscopy, UV–Vis spectrophotometer and field emission scanning electron microscopy (FE-SEM) images. The antifungal activity was analyzed in planktonic cells and 48h-biofilm of C. albicans by colony forming units (CFU) counting, confocal laser and FE-SE microscopies. Statistical analysis was carried out using SPSS software. Morphological and structural modifications of Ag₃PO₄ were observed upon recycling. After 4 recycles, the material maintained its photodegradation property; an eightfold increase in the efficiency of Ag₃PO₄ was observed in planktonic cells and a two fold increase in biofilm when irradiated under visible light. Thus, higher antifungal effectiveness against C. albicans was obtained when associated with visible-light irradiation.     

Nanoraspberry-like palladium/spongy nickel oxide for electrooxidation of five light fuels

The spongy nickel oxide (SNO) was synthesized the solution combustion method. The SNO was selected as a promoter to boost the catalytic activity of nanoraspberry-like palladium (NRPd) toward electrooxidation of five light fuels (LFs): methanol, ethanol, formaldehyde, formic acid, and ethylene glycol. The X-ray powder diffraction, Fourier-transform infrared spectroscopy (FT-IR), scanning electron microscopy, and field emission scanning electron microscope techniques were used for the materials characterization. In comparison with nonpromoted Pd, the NRPd-SNO electrocatalyst shown an excellent efficiency in parameters like the electrochemical active surface area and anti-CO poisoning behavior. The turnover data and the parameters, including reaction order, activation energy, and the coefficients of electron transfer and diffusion, were evaluated for the each process of LFs electrooxidation. The outcome for NRPd-SNO activity toward LFs electrooxidation was compared to some reported electrodes. The SNO increases the removal of intermediates created in the oxidation of LFs that can poison the surface of palladium catalyst. This is due to the presence of the lattice oxygens in SNO structure and Ni switching between its high and low valances. The compatibility of the adsorption process of LFs on the surface of the NRPd-SNO catalyst with different isotherms was determined by studying the Tafel polarization and calculating the surface coverage.     

催化共振光散射法测定空气中痕量甲醛的研究

吖啶橙分子聚集体微粒可在513nm波长处出现最大的共振光散射强度(RLS)。在稀硫酸介质中,甲醛能催化溴酸钾氧化吖啶橙的反应,促使其RLS强度减弱。在最佳实验条件下,甲醛质量浓度ρ在0.020～0.25μg/mL的范围内与△I值呈良好的线性关系,线性回归方程为△I=1113.99ρ+49.23,线性相关系数r为0.9986。本法与国标法进行对照,在置信度等于95%时,用Cochran检验,两种方法间不存在显著性差异,方法操作简单、灵敏度高,用于室内外空气中甲醛测定,结果满意。     

Highly transparent Yb:Y2O3 ceramics obtained by solid-state reaction and combined sintering procedures

(Y_0.87-xLa_0.1Zr_0.03Yb_x)₂O₃ (x?=?0.02, 0.04, 0.05) transparent ceramics were obtained by solid-state reaction and combined sintering procedures with La₂O₃ and ZrO₂ as sintering additives. A method based on two-step intermediate sintering in air followed by vacuum sintering was applied in order to control the densification and grain growth of the samples during the final sintering process. The results indicate that La₂O₃ and ZrO₂ co-additives can improve the microstructure and optical properties of Yb:Y₂O₃ ceramics at relatively low sintering temperature. On the other hand, the addition of Zr⁴⁺ ions leads to the formation of dispersed scattering volumes in the ceramic bodies. Transmittance of 78.8% was measured for the 2.0?at% Yb:Y₂O₃ ceramic sample at the wavelength of 1100?nm. The spectroscopic properties of Yb:Y₂O₃ ceramics were investigated at room temperature. The obtained results show that the absorption cross-section at 978?nm is in the range of 2.08?×?10^–20 to 2.36?×?10^–20 cm², whereas the emission cross-section at 1032?nm is ~1.0?×?10^–20 cm².     

腔磁力系统中的诱导透明和快慢光传播

为了在腔磁力系统中实现可控的磁子诱导透明、磁力诱导透明以及快慢光传播,建立了一个混合腔磁力系统.该系统由一个含有YIG球的微波腔和在z方向对球施加一个均匀的偏置磁场组成,并用强泵浦场驱动磁子和弱探测场驱动微波腔.研究表明,通过调节腔与磁子之间的相互作用强度和微波腔与磁子的耗散比,可以增加磁子诱导透明(MIT)、磁力诱导透明(MMIT)的效果和提高快慢光传播的速度.该研究结果可为磁力诱导放大、量子光学操纵和量子信息存储以及灵敏光开关的研究提供参考.     

Evolution of core–rim structures and phase transformations in infra-red transmitting Y-α-SiAlON ceramics

Core–rim structures were observed as common features in Y-α-SiAlON ceramics hot-pressed between 1550?1950 °C. We found most dopants were taken into α’-rims, and a transition layer grown first on α-cores from liquid-phase over-saturated with metal solutes. Elongated β’-grain were formed as minor phase with α’- or AlN-cores thus only after the α’ matrix had consumed up all Y solutes, revealing that the α’ → β’ transformation is controlled by the transient liquid-phase and similar defects and dangling bonds could be detected in both SiAlON phases by cathodoluminescence. Quantitative assessment of Y_m/3Si_12?(m+n)Al_m+nO_nN_16?n demonstrates the multiphase evolution, initiated by over-saturation of Y solutes at low temperatures thus retaining α-phase as cores to lower the infra-red transmittance, dictated by homogenization of Al solutes at higher temperature. The elimination of those phase boundaries leads to better dopant and sintering design for achieving transparent and high-performance SiAlON ceramics.